Poxenamel 2/C

High-solid polyurethane enamel, made from hydroxylated acrylic resin binder and zinc phosphate corrosion-inhibiting pigment. Combined finishing topcoat and primer, for direct application on metal.

Recommended as a finish and primer in one, to be applied direct on metal, for excellent chemical and strong weather resistance are desired, leaving a smooth, semi-gloss, decorative finish.
Excellent adhesion on steel and galvanized surfaces.

Uso: Interior-Exterior
Tamaños: 15 Litres, 4 Litres
Acabados
Gloss
Rendimiento
7,2 m²/l colour dependant.
Dilución
Thinner D-17
Thinner D-71
Limpieza
Thinner D-17
Thinner D-71
Secado
2-3 hours
Repintado
5 hours
Sólidos en volumen
58 ± 2 %
Espesor
80 microns
Colores
  • Leaves a hard paint film
  • Good adhesion on steel and galvanized steel
  • Great opacity
  • Protects metal against oxidation
  • Good gloss and colour retention
c3-pinturas-juno__en
Anti-corrosive system C-3

Spray application: D-17. Brush/roller application: D-71. (See TDS for brush and roller application).
IRON AND STEEL. Abrasive blasting up to Sa 2 ½ grade according to ISO 8501-1. Roughness profile 30µ. Loose paint coatings, mill scale, rust and foreign matter will be removed.
Apply POXENAMEL 2/C immediately after blasting to prevent any type of contamination.
GALVANIZED SURFACES.
Eliminate the rust typical of galvanizing by washing with detergents, fresh water and abrasive synthetic fibres. If necessary, sand to refine the surface.
Stir component A in its container and once homogenized add component B slowly to it (in the indicated proportions), while mechanically stirring at low speed. Shake for 2 minutes until perfectly homogenized. Let the mixture rest for 10 minutes before use to let air out. Do not use the product after its indicated portlife of 4 hours.
For more information see technical datasheet.